Spheroidizing elements are generally divided into three groups according to their spheroidizing effect. The first group: Mg, Y, Ce, La, Pr, Sm, Dy, Ho, Er. The second group: Ba, Li, Cs, Rb, Sr, Th, K, Na. The third group: Al, Zn, Cd, Sn. The first group has the strongest spheroidization ability, followed by the second group, and the third group the weakest. When magnesium is used as the spheroidizing element, the third group of elements tends to produce de-spheroidization. Despheroidizing elements: Sulfur and oxygen are common despheroidizing elements in cast iron. In addition, Ti, Al, B, As, Pb, Sn, Sb, Bi, Te, Se, etc. are common despheroidizing elements in molten iron .
1. How to choose nodulizer
Spheroidizing agent and inoculant are the most important materials in the spheroidizing process. In addition to stable quality, xinyuanzhu group recommends to consider the following factors when choosing a suitable spheroidizing agent.
1.1 Spheroidizing temperature: If the spheroidizing temperature is 1480℃, the spheroidizing reaction will be more violent, resulting in lower magnesium absorption rate. In order to make the spheroidizing reaction stable, a spheroidizing agent with relatively high calcium content can be selected. If the spheroidizing temperature is 1480°C, a spheroidizing agent with a relatively low calcium content can be used.
1.2 Treatment bag size: If the height-to-diameter ratio of the treatment bag is 1:1, the loss of magnesium vapor will cause the reduction of magnesium absorption rate. It is recommended to use a spheroidizing agent with a higher calcium content.
If the height-to-diameter ratio of the treatment package is 2:1, the spheroidization reaction will be relatively stable, the magnesium vapor will diffuse into the molten iron, and the magnesium absorption rate will be improved.
1.3 Spheroidization process: If the cover method is not used, the smoke generated by the spheroidization reaction will enter the atmosphere and produce dazzling white light. In order to stabilize the spheroidizing reaction, a spheroidizing agent with low magnesium and high calcium can be used.
If you use the lid-laden process, the molten iron will not splash and produce less smoke. You can use a high-magnesium and low-calcium spheroidizing agent to reduce the amount and reduce the cost of spheroidization.
1.4 Processing weight: If the weight of the molten iron is less than 500kg, then a spheroidizing agent with a smaller particle size can be used, and it is recommended to use a spheroidizing agent with a particle size of less than 12mm. If the weight of the molten iron is 500~1000kg, a spheroidizing agent with a larger particle size can be used, such as a spheroidizing agent with a particle size of 3-25mm. If the weight of the molten iron is more than 1000kg, the spheroidizing agent of 4~32mm can be used.
1.5 Silicon content: If the process yield rate of the cast product is low or the scrap rate is high, you want to melt it by adding more charge and scrap, and the final casting has strict requirements on the silicon content of the molten iron. Under the premise that the inoculation volume cannot be further reduced, a low-silicon spheroidizing agent can be used for treatment, which can increase the refurbishment material by 8% to 15%, which can reduce the production cost of the foundry.
1.6 Sulfur content of raw iron liquid: If the sulfur content of the raw iron liquid is high, if the desulfurization treatment is not carried out, a spheroidizing agent with high magnesium and high rare earth is required, and the addition amount will be higher. If the sulfur content of the raw iron liquid is low, The spheroidizing agent with low magnesium and rare earth can be used, and the added amount will be lower, and the cost of the spheroidizing agent with low magnesium and rare earth will be cheaper.

2. Different spheroidization methods
The xinyuanzhu group has summarized the following in the casting process: in-pack processing method (including direct punching method, sandwich method and cover method), in-mold spheroidization method, flow method, pure magnesium treatment process (including subcontracting method and Cored wire method). The advantages and disadvantages of these spheroidization methods are briefly introduced below.
2.1 In-package processing method: This is the most common spheroidization process, which has a wide range of applications. This process can be used for automotive parts as small as a few kilograms and wind power parts as large as tens of tons. The magnesium absorption rate is highest in the cover method, followed by the sandwich method. The disadvantage is that the current degree of automation is not high, and some domestic equipment factories are developing automatic feeding systems.
2.2 Type internal spheroidization method: There are not many foundries using this process, because the shortcomings of this process are obvious. The slag produced by the spheroidization process sometimes enters the cavity, causing slag inclusion defects and waste products. In addition, this spheroidizing process has higher requirements on the temperature and flow rate of the molten iron, otherwise the spheroidization will be uneven.
2.3 Flow method: As the name implies, the flow method is spheroidizing by flowing molten iron through a spheroidizing chamber filled with spheroidizing agent. At present, this process is not used too much. The advantage is that the degree of automation is relatively high; the disadvantage is that it has strict requirements on the temperature and flow rate of the molten iron.
2.4 Pure magnesium spheroidization process: sometimes called high-magnesium spheroidization process, currently there are two main forms, subcontracting method and cored wire method. The advantage of this method is that it has a higher degree of automation and is also conducive to environmental protection; the disadvantage is that the magnesium absorption rate is low, and it produces more smoke and slag

3. Matters needing attention in the production of ductile iron
Xinyuanzhu Group combined the problems that occurred in the production of ductile iron and summarized the following points for attention.
3.1 The sulfur content and other trace elements of the original molten iron should not be too high. If the sulfur content and the content of other trace elements in the original molten iron are too high, more spheroidizing agent is needed or a spheroidizing agent with a higher rare earth content is required, so the cost of the spheroidizing agent will increase, and excessive spheroidizing The agent will cause more slag, which is not conducive to the stability of casting quality. Too much rare earth content will easily produce fragmented graphite on large-section castings.
3.2 The stability of spheroidization. The spheroidizing process is a key process in the production of nodular cast iron. Only when the spheroidizing process is stable can the quality of the casting be stable. For different products, different sulfur content of the original molten iron, how much nodulizer, inoculant, etc. should be added, must be written into the work instruction and strictly implemented.
3.3 Avoid long waiting times. After the spheroidization inoculation, pouring should be carried out immediately. Because over time, the residual magnesium will burn and the inoculation effect will decline.
3.4 Avoid excessively high residual magnesium content. Higher residual magnesium content will increase the shrinkage tendency of castings. For general ductile iron, the residual magnesium content (mass fraction) should be controlled within 0.035%~0.045%, and for high nickel ductile iron, the residual magnesium content should be controlled within 0.06% ~0.07%.
3.5 Use better inoculants for castings with higher requirements. For wind power parts and high-speed rail parts with higher requirements, the flow inoculant with stronger inoculation effect should be selected. Its characteristic is that it can significantly increase the number of graphite spheres, and the graphite spheres are rounded.

Xinyuanzhu Group specializes in the production of Ductile iron castings, Pig iron gray iron casting, Steel casting, Brass Casting, Malleable Iron Casting, and undertakes batch casting processing of castings. Welcome guests to cooperate with pictures or samples